NiCr A286

Stainlesss Steel Wire

Spring Works Utah specializes in the custom manufacture of wire springs, flat springs, and wire products using NiCr A286 Stainless Steel Wire material. Our extensive inventory and design experience makes us a resource for customer requests as well as a preferred supplier to spring manufacturers worldwide. We know choosing the right material can be challenging and many times the most important aspect of your design. We will assist you in picking the best material for your specific application, all at the right price.

 

 

Choosing the Right Springs Manufacturer Matters!

Put Us To Work For You!

 

*Mobile: To view complete table - scroll horizontally

Technical Specifications of Stainless Steel Wire NiCr A286

Specifications Key Features Chemical Composition
AMS 5688
ASTM A313
ASTM A580
BS 970
BS 2056
Good mechanical properties and corrosion resistance.
Element Min % Max %
C - 0.12
Mn - 2.00
P - 0.045
S - 0.03
Si - 1.00
Cr 17.00 19.00
Ni 8.00 10.00

 

*Mobile: To view complete table - scroll horizontally

Technical Specifications of Stainless Steel Wire NiCr A286

Maximum Temperature 500°F 260°C
Melting Point 2590°F 1420°C
Minimum Size 0.005 in 0.130 mm
Maximum Size 0.375 in 9.500 mm
Modulus of Elasticity 27195 ksi 187.5 kN/mm²
Modulus of Rigidity 10196 ksi 70.3 kN/mm²
Density 0.286 lb/in3 7.920 g/cm3
Relative Strength Medium
Fatigue Applications Good
Rockwell Hardness C35-45
Conductivity 2
Typical Surface B

 

*Mobile: To view complete table - scroll horizontally

Technical Specifications of Stainless Steel Wire NiCr A286

E Mpa Young's Modulus These factors can vary with cold work, heat treating and operational stress.
E psi
G Mpa Modulus of Rigidity
G psi
Conductivity % IACS
Surface Min Typical Surface Quality A Maximum defect depth: 0 to 0.5% of d or t
B Maximum defect depth: 1.0% of d or t
C Defect depth:less that 3.5% of d or t
Min Size Sizes commonly available for wire or strip Special sizes may be available at additional cost.
Max Size
Max Temp Maximum service temperature May vary due to operating stress

Information is for Reference Purposes Only. Factors can vary with cold work, stress relieving and operational stress. Variations may be minor but should be considered for critical properties.

 

*Mobile: To view complete table - scroll horizontally

NiCr A286 Wire Springs

NiCr A286 Flat Springs

NiCr A286 Wire Products

NiCr A286 Torsion Springs
NiCr A286 Conical Springs
NiCr A286 Tapered Springs
NiCr A286 Barrel Springs
NiCr A286 Die Springs
NiCr A286 Garter Springs
NiCr A286 Cable Springs
NiCr A286 Wave Springs
NiCr A286 Coil Springs
NiCr A286 Valve Springs
NiCr A286 Micro Springs
NiCr A286 Helical Springs
NiCr A286 Spring Clips
NiCr A286 Spiral Springs
NiCr A286 Power Springs
NiCr A286 Wave Washers
NiCr A286 Curved Washers
NiCr A286 Retaining Rings
NiCr A286 Volute Springs
NiCr A286 Bow Springs
NiCr A286 Clock Springs
NiCr A286 Wire Forms
NiCr A286 Wire Bending
NiCr A286 Wire Rings
NiCr A286 Wire Forming
NiCr A286 Wire Products
NiCr A286 S-Hooks

Stainless Steel Wire NiCr A286