Hard Drawn

Leading Manufacturer of Custom Springs Worldwide

Deprecated: Methods with the same name as their class will not be constructors in a future version of PHP; plgContentJabookmark has a deprecated constructor in /home2/sprinhb6/public_html/springworksutah/plugins/content/jabookmark/jabookmark.php on line 26

Hard Drawn

Carbon Steel Wire

Spring Works Utah specializes in the custom manufacture of wire springs, flat springs, and wire products using Hard Drawn Carbon Steel Wire material. Our extensive inventory and design experience makes us a resource for customer requests as well as a preferred supplier to spring manufacturers worldwide. We know choosing the right material can be challenging and many times the most important aspect of your design. We will assist you in picking the best material for your specific application, all at the right price.

 

 

 

Choosing the Right Springs Manufacturer Matters!

Put Us To Work For You!

 

*Mobile: To view complete table - scroll horizontally

Technical Specifications of Carbon Steel Wire Hard Drawn

Specifications Key Features Chemical Composition
AMS 5688
ASTM A313
ASTM A580
BS 970
BS 2056
Good mechanical properties and corrosion resistance.
Element Min % Max %
C - 0.12
Mn - 2.00
P - 0.045
S - 0.03
Si - 1.00
Cr 17.00 19.00
Ni 8.00 10.00

 

*Mobile: To view complete table - scroll horizontally

Technical Specifications of Carbon Steel Wire Hard Drawn

Maximum Temperature 500°F 260°C
Melting Point 2590°F 1420°C
Minimum Size 0.005 in 0.130 mm
Maximum Size 0.375 in 9.500 mm
Modulus of Elasticity 27195 ksi 187.5 kN/mm²
Modulus of Rigidity 10196 ksi 70.3 kN/mm²
Density 0.286 lb/in3 7.920 g/cm3
Relative Strength Medium
Fatigue Applications Good
Rockwell Hardness C35-45
Conductivity 2
Typical Surface B

 

*Mobile: To view complete table - scroll horizontally

Technical Specifications of Carbon Steel Wire Hard Drawn

E Mpa Young's Modulus These factors can vary with cold work, heat treating and operational stress.
E psi
G Mpa Modulus of Rigidity
G psi
Conductivity % IACS
Surface Min Typical Surface Quality A Maximum defect depth: 0 to 0.5% of d or t
B Maximum defect depth: 1.0% of d or t
C Defect depth:less that 3.5% of d or t
Min Size Sizes commonly available for wire or strip Special sizes may be available at additional cost.
Max Size
Max Temp Maximum service temperature May vary due to operating stress

Information is for Reference Purposes Only. Factors can vary with cold work, stress relieving and operational stress. Variations may be minor but should be considered for critical properties.

 

*Mobile: To view complete table - scroll horizontally

Hard Drawn Wire Springs

Hard Drawn Flat Springs

Hard Drawn Wire Products

Hard Drawn Torsion Springs
Hard Drawn Conical Springs
Hard Drawn Tapered Springs
Hard Drawn Barrel Springs
Hard Drawn Die Springs
Hard Drawn Garter Springs
Hard Drawn Magazine Springs
Hard Drawn Cable Springs
Hard Drawn Wave Springs
Hard Drawn Coil Springs
Hard Drawn Valve Springs
Hard Drawn Micro Springs
Hard Drawn Helical Springs
Hard Drawn Spring Clips
Hard Drawn Spiral Springs
Hard Drawn Power Springs
Hard Drawn Wave Washers
Hard Drawn Curved Washers
Hard Drawn Retaining Rings
Hard Drawn Volute Springs
Hard Drawn Bow Springs
Hard Drawn Battery Contacts
Hard Drawn Clock Springs
Hard Drawn Wire Forms
Hard Drawn Wire Bending
Hard Drawn Wire Rings
Hard Drawn Wire Forming
Hard Drawn Wire Products
Hard Drawn S-Hooks

Carbon Steel Wire Hard Drawn